materials for Alloy Cast Iron
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 5.54 - 7.81 g/cc | 0.200 - 0.282 lb/in3 | Average value: 7.17 g/cc Grade Count:84 |
Mechanical Properties | Metric | English | Comments |
Hardness, Brinell | 110 - 807 | 110 - 807 | Average value: 262 Grade Count:77 |
Hardness, Knoop | 162 - 906 | 162 - 906 | Average value: 252 Grade Count:34 |
Hardness, Rockwell C | 11.6 - 65 | 11.6 - 65 | Average value: 31.8 Grade Count:11 |
Hardness, Vickers | 151 - 871 | 151 - 871 | Average value: 238 Grade Count:34 |
Tensile Strength, Ultimate | 90.0 - 1650 MPa | 13100 - 240000 psi | Average value: 632 MPa Grade Count:86 |
Tensile Strength, Yield | 172 - 1450 MPa | 24900 - 210000 psi | Average value: 520 MPa Grade Count:72 |
Elongation at Break | 0.20 - 40 % | 0.20 - 40 % | Average value: 9.06 % Grade Count:66 |
Reduction of Area | 2.0 - 10 % | 2.0 - 10 % | Average value: 5.38 % Grade Count:13 |
Modulus of Elasticity | 63.0 - 240 GPa | 9140 - 34800 ksi | Average value: 156 GPa Grade Count:38 |
Compressive Yield Strength | 331 - 2520 MPa | 48000 - 365000 psi | Average value: 1050 MPa Grade Count:23 |
Poissons Ratio | 0.25 - 0.37 | 0.25 - 0.37 | Average value: 0.283 Grade Count:23 |
Fatigue Strength | 68.9 - 510 MPa | 10000 - 74000 psi | Average value: 334 MPa Grade Count:18 |
Fracture Toughness | 44.0 - 110 MPa-m½ | 40.0 - 100 ksi-in½ | Average value: 81.4 MPa-m½ Grade Count:7 |
Machinability | 0.00 - 125 % | 0.00 - 125 % | Average value: 41.7 % Grade Count:3 |
Shear Modulus | 60.2 - 67.6 GPa | 8730 - 9800 ksi | Average value: 64.5 GPa Grade Count:23 |
Shear Strength | 200 - 1480 MPa | 29000 - 215000 psi | Average value: 712 MPa Grade Count:15 |
Charpy Impact | 0.100 - 40.0 J | 0.0738 - 29.5 ft-lb | Average value: 15.3 J Grade Count:13 |
Charpy Impact, Unnotched | 2.70 - 200 J | 1.99 - 148 ft-lb | Average value: 78.0 J Grade Count:22 |
Electrical Properties | Metric | English | Comments |
Electrical Resistivity | 0.00000500 - 110 ohm-cm | 0.00000500 - 110 ohm-cm | Average value: 6.11 ohm-cm Grade Count:18 |
Magnetic Permeability | 100 - 750 | 100 - 750 | Average value: 410 Grade Count:5 |
Thermal Properties | Metric | English | Comments |
CTE, linear | 7.75 - 19.3 m/m-C | 4.31 - 10.7 in/in-F | Average value: 12.7 m/m-C Grade Count:29 |
Specific Heat Capacity | 0.506 J/g-C | 0.121 BTU/lb-F | Average value: 0.506 J/g-C Grade Count:3 |
Thermal Conductivity | 11.3 - 53.3 W/m-K | 78.4 - 370 BTU-in/hr-ft2-F | Average value: 26.6 W/m-K Grade Count:23 |
Melting Point | 1120 - 1310 C | 2050 - 2390 F | Average value: 1150 C Grade Count:8 |
Maximum Service Temperature, Air | 649 C | 1200 F | Average value: 649 C Grade Count:6 |
Minimum Service Temperature, Air | -59.4 - -30.0 C | -75.0 - -22.0 F | Average value: -34.9 C Grade Count:6 |
Component Elements Properties | Metric | English | Comments |
Aluminum, Al | 0.050 - 25 % | 0.050 - 25 % | Average value: 3.26 % Grade Count:7 |
Antimony, Sb | 0.0020 - 0.20 % | 0.0020 - 0.20 % | Average value: 0.0174 % Grade Count:7 |
Arsenic, As | 0.020 % | 0.020 % | Average value: 0.0200 % Grade Count:6 |
Bismuth, Bi | 0.0020 % | 0.0020 % | Average value: 0.00200 % Grade Count:6 |
Boron, B | 0.00060 % | 0.00060 % | Average value: 0.000600 % Grade Count:6 |
Cadmium, Cd | 0.0050 % | 0.0050 % | Average value: 0.00500 % Grade Count:6 |
Carbon, C | 0.40 - 4.1 % | 0.40 - 4.1 % | Average value: 3.25 % Grade Count:77 |
Cerium, Ce | 0.0050 - 0.20 % | 0.0050 - 0.20 % | Average value: 0.102 % Grade Count:24 |
Chromium, Cr | 0.030 - 35 % | 0.030 - 35 % | Average value: 2.48 % Grade Count:60 |
Copper, Cu | 0.020 - 10 % | 0.020 - 10 % | Average value: 1.23 % Grade Count:50 |
Iron, Fe | 49 - 96.2 % | 49 - 96.2 % | Average value: 84.7 % Grade Count:85 |
Lead, Pb | 0.0020 % | 0.0020 % | Average value: 0.00200 % Grade Count:6 |
Magnesium, Mg | 0.020 - 0.060 % | 0.020 - 0.060 % | Average value: 0.0425 % Grade Count:30 |
Manganese, Mn | 0.10 - 4.5 % | 0.10 - 4.5 % | Average value: 0.679 % Grade Count:74 |
Molybdenum, Mo | 0.00 - 16 % | 0.00 - 16 % | Average value: 0.759 % Grade Count:54 |
Nickel, Ni | 0.050 - 43 % | 0.050 - 43 % | Average value: 8.62 % Grade Count:59 |
Oxygen, O | 0.0050 % | 0.0050 % | Average value: 0.00500 % Grade Count:6 |
Phosphorus, P | 0.015 - 0.30 % | 0.015 - 0.30 % | Average value: 0.0782 % Grade Count:67 |
Selenium, Se | 0.030 % | 0.030 % | Average value: 0.0300 % Grade Count:6 |
Silicon, Si | 0.50 - 17 % | 0.50 - 17 % | Average value: 2.77 % Grade Count:85 |
Sulfur, S | 0.0020 - 0.15 % | 0.0020 - 0.15 % | Average value: 0.0463 % Grade Count:57 |
Tellurium, Te | 0.020 % | 0.020 % | Average value: 0.0200 % Grade Count:6 |
Tin, Sn | 0.010 - 0.30 % | 0.010 - 0.30 % | Average value: 0.0538 % Grade Count:12 |
Titanium, Ti | 0.040 % | 0.040 % | Average value: 0.0400 % Grade Count:6 |
Vanadium, V | 0.10 - 2.0 % | 0.10 - 2.0 % | Average value: 0.478 % Grade Count:9 |